Description/kawalan
Parameter teknikal
Elektrod grafit HPterutamanya diperbuat daripada coke petroleum dan jarum kok, mampu membawa ketumpatan semasa18-25 a/cm2. Ia direka untuk pembuatan keluli arka elektrik yang tinggi.
Sifat khas elektrod grafit
| Sifat | Kedudukan | Unit | UHP | Hp | Rp | |
| 300-600 mm | 650-800 mm | 300-800 mm | 300-800 mm | |||
| Rintangan khusus | Badan | μΩm | 4.8-5.8 | 4.6-5.8 | 5.8-6.6 | 7.8-8.8 |
| Puting | 3.8-4.5 | 3.8-4.5 | 4.2-5.0 | 5.0-6.5 | ||
| Lenturan Strengh | Badan | MPA | 10.0-14.0 | 10.0-14.0 | 10.0-13.0 | 7.0-12.0 |
| Puting | 20.0-26.0 | 20.0-26.0 | 18.0-22.0 | 15.0-20.0 | ||
| Modulus Young | Badan | GPA | 9.0-13.0 | 10.0-14.0 | 8.0-12.0 | 7.0-9.3 |
| Puting | 15.0-18.0 | 15.0-18.0 | 14.0-16.0 | 12.0-14.0 | ||
| Ketumpatan pukal | Badan | g/cm3 | 1.68-1.74 | 1.70-1.74 | 1.62-1.66 | 1.53-1.56 |
| Puting | 1.77-1.82 | 1.78-1.84 | 1.74-1.80 | 1.70-1.74 | ||
| Cte (100-600 ijazah) | Badan | ×10 -6/ﾟC | 1.1-1.4 | 1.1-1.4 | 1.6-1.9 | 2.2-2.6 |
| Puting | 0.9-1.2 | 0.9-1.2 | 1.1-1.4 | 2.0-2.5 | ||
| Kandungan abu | % | 0.3 | 0.3 | 0.3 | 0.5 |